LG ABS TR551
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SsniMP_LG-ABS-TR551.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description High Transparency, High Rigidity, High Hardness, Chemical Resistance Applications Electric&Electronic Products |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 8.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 56.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 30 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2550 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 90.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20 mm | 130 | J/m | |
| 23°C, 6.40 mm | 130 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm) | 86.0 | °C | ASTM D648 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | 1.9 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transparency | 90 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 200 to 220 | °C | |
| Front Temperature | 210 to 230 | °C | |
| Nozzle Temperature | 210 to 240 | °C | |
| Processing (Melt) Temp | 210 to 240 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C | |
| Back Pressure | 29.4 to 58.8 | MPa | |
| Screw Speed | < 80 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TPV Elastoprene® N55A-E | ELASTORSA Elastomeros Riojanos S.A. | PP+EPDM | TPV Elastoprene® |
| Braskem PE HF2007 | Braskem | LLDPE | Braskem PE |
| GLS PP YN08 | GLS Polymers Pvt. Ltd. | PP, Unspecified | GLS PP |
| Jiangsu Sinarise ZM928 | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| Axiall PVC 3265 | Axiall Corporation | PVC, Rigid | Axiall PVC |