PLUSTEK PB145
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | PLUSTEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SsGsBz_PLUSTEK-PB145.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| General puprpose Polyamide 6 for Fast Cycle Injection Moulding applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 1.3 - 1.7 | % | ASTM D955 |
| -- | 1.3 - 1.7 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 9.5 | % | ASTM D570 |
| Saturated, 23°C | 9.5 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 3.0 | % | ASTM D570, ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 120 | ASTM D785 | |
| R scale | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 90.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | > 10 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2600 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 100 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 3.5 | kJ/m² | ISO 179 |
| 23°C | 5.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ISO 179 | |
| 23°C | No Break | ISO 179 | |
| Notched Izod Impact | |||
| -30°C | 35 | J/m | ASTM D256 |
| 23°C | 50 | J/m | ASTM D256 |
| -30°C | 3.5 | kJ/m² | ISO 180 |
| 23°C | 5.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 185 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 80.0 | °C | ASTM D648, ISO 75-2/A |
| Maximum operating temperature- Short Peaks Operation | 180 | °C | |
| Maximum Continuous Use Temperature | 80 | °C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability | 17 | mm/min | FMVSS 302 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 218 | °C | ISO 11357-3, ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Dielectric Strength | 100 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.50 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-2 | UL 94 | |
| 3.00 mm | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 220 - 260 | °C | |
| Middle Temperature | 230 - 265 | °C | |
| Front Temperature | 250 - 270 | °C | |
| Mold Temperature | 55.0 - 95.0 | °C | |
| Injection Pressure | 70.0 - 105 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 30.0 - 70.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 50 to 75 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® HHM TR-144 | Saudi Polymers Company | HDPE | Marlex® |
| SHIN-A ZCP-250M75 | SHIN-A T&C | Epoxy | SHIN-A |
| Witcom PA66 6LC-EM-HS | Witcom Engineering Plastics B.V. | Nylon 66 | Witcom PA66 |
| Petrothene® NA860 | LyondellBasell Industries | LDPE | Petrothene® |
| Sylvin 9925-70UV Green 3162 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |