Asrene® UF 1810T
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Chandra Asri Petrochemical |
| Trademark: | Asrene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Sr2CVS_Asrene-UF-1810T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Asrene®UF 1810T is a linear low density polyethylene product,. It is available in North America, Europe or Asia Pacific. Asrene®UF 1810T applications include bags/linings and movies. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 0.11 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 30 µm, blown film | 50.0 | MPa | ASTM D882 |
| TD : Broken, 30 µm, blown film | 24.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 30 µm, blown film | 700 | % | ASTM D882 |
| TD : Broken, 30 µm, blown film | 850 | % | ASTM D882 |
| Dart Drop Impact (30 µm, Blown Film) | 100 | g | ASTM D1709 |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 30.0 µm | 24.5 | kN/m | ASTM D1922 |
| TD : 30.0 µm | 196.1 | kN/m | ASTM D1922 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blocking - Blown Film | 65.0 | g/100 cm² | ASTM D3354 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 104 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 30.0 µm, Blown Film) | 60 | ASTM D2457 | |
| Clarity (50.0 µm, Blown Film) | 63.0 | ASTM D1746 | |
| Haze (30.0 µm, Blown Film) | 15 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 - 200 | °C |
| Extrusion instructions |
|---|
| Blow-up Ratio: 1.5 to 3.5 |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ GV-819.G001-1001 | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| S&E Wire & Cable GTPE-2272ALC | S&E Specialty Polymers, LLC | TPE | S&E Wire & Cable |
| Monprene® IN-12250 | Teknor Apex Company | TPE | Monprene® |
| Lupox® GP1000SB | LG Chem Ltd. | PBT | Lupox® |
| Rotuba CAB B902 (11% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |