Zythane® 5085A
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Alliance Polymers & Services |
| Trademark: | Zythane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SqOb4G_Zythane-5085A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Zythane 5085A is a polyester--based TPU specifically formulated for extrusion applications. It exhibits excellent abrasion resistance and toughness and has good hydrolytic stability, oil, fuel and solvent resistance. It is supplied uncolored in pellet form. Typical Applications: Zythane 5085A applications include among others spiral and pneumatic tubing, round and V belting, blow molded bellows. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance | 23.0 | mg | ASTM D1044 |
| Abrasion - DIN | 20 | mm³ | DIN 53516 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 5.00 | MPa | ASTM D412 |
| 300% strain | 14.0 | MPa | ASTM D412 |
| Tensile Strength (Break) | 43.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 620 | % | ASTM D412 |
| Tear Strength 1 | 81.4 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 24°C, 22 hr | 23 | % | ASTM D395B |
| 70°C, 72 hr | 33 | % | ASTM D395B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -31.1 | °C | DSC |
| Vicat Softening Temperature | 110 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | HB | UL 94 | |
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 180 | °C | |
| Middle Temperature | 195 | °C | |
| Front Temperature | 200 | °C | |
| Nozzle Temperature | 200 - 215 | °C | |
| Processing (Melt) Temp | 205 - 210 | °C | |
| Mold Temperature | 25.0 - 60.0 | °C | |
| Back Pressure | 0.500 - 1.00 | MPa | |
| Screw Speed | 60 - 200 | rpm | |
| Clamp Tonnage | 4.1 - 6.9 | kN/cm² |
| Injection instructions |
|---|
| Injection Speed: >.4 in/sec |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 4.0 | hr | |
| Cylinder Zone 1 Temp. | 180 | °C | |
| Cylinder Zone 2 Temp. | 195 | °C | |
| Cylinder Zone 3 Temp. | 200 | °C | |
| Die Temperature | 215 | °C |
| Extrusion instructions |
|---|
| Gate Temperature: 200°C (392°F) |
| Note Message | |
|---|---|
| 1 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnoform® 300 LS | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| Wah Hong DAP WH-9100- BLK C | Wah Hong Industrial Corp. | DAP | Wah Hong DAP |
| Unichem 7012N-02 | Colorite Polymers | PVC, Unspecified | Unichem |
| Kemid Polyetherimide Film | Saint Gobain - Norton | PEI | Kemid |
| Sylvin 9780-60 Green 3205 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |