Latilub 80-10T K/15
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latilub |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SpaFCc_Latilub-80-10T-K-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Self-lubricating product based on Polyphenylene Sulphide (PPS). PTFE. Carbon fibre. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.30 to 0.50 | % | |
| Flow : 2.00 mm | 0.20 to 0.35 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 16000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 130 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 0.70 | % | ISO 527-2/5 |
| Coefficient of Friction | ASTM D3702 | ||
| vs. Itself - Dynamic | 0.21 | ||
| vs. Itself - Static | 0.26 | ||
| Wear Factor | 8.00E-10 | (m³/h)/(N·m·h) | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 20 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 45 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 280 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 265 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 255 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 290 to 310 | °C | |
| Mold Temperature | 130 to 150 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tislamid® PA66 PA66 UNR FR HF | Tisan | Nylon 66 | Tislamid® PA66 |
| Trademark PP PPH2000MA | Trademark Plastics Corporation | PP Homopolymer | Trademark PP |
| ALTECH® PP-H A 2030/652 GF30 UV CP | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| Axiall PVC 7456 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Karina GRAY PVC COMPOUND 700D18/234-C-IS-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |