SABIC® LDPE HP0722N
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | SABIC Americas, Inc. |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SomG4M_SABIC-LDPE-HP0722N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Description HP0722N is Low Density Polyethylene grade suitable for producing medium duty films and contains no slip and antiblock additives. It gives good toughness and optical properties in the film. Typical Applications HP0722N can be used for medium duty bags, shrink films, shopping bags, lamination films and frozen food packaging. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 0.75 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 50 µm, blown film | 180 | MPa | ASTM D882 |
| 1% secant, TD : 50 µm, blown film | 200 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm, blown film | 10.0 | MPa | ASTM D882 |
| TD : Yield, 50 µm, blown film | 9.00 | MPa | ASTM D882 |
| MD : Broken, 50 µm, blown film | 27.0 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 23.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 400 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 650 | % | ASTM D882 |
| Dart Drop Impact (50 µm, Blown Film) | 200 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, blown film | 350 | g | ASTM D1922 |
| TD : 50 µm, blown film | 280 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Blown Film) | 60 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 9.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Blow-up Ratio | 2.50 - 4.00 | ||
| Properties have been measured by producing 50 µ film with 2.5 BUR using 100% HP0722N. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 - 185 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA612 A5G7301 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 612 | Shandong PA612 |
| UNIVAL™ DMDA-6400 NT 7 | The Dow Chemical Company | HDPE | UNIVAL™ |
| Enviramid® N1315STHL BK | Ravago Manufacturing Americas, LLC | Nylon 66 | Enviramid® |
| Lupoy® SR3108FM | LG Chem Ltd. | PC | Lupoy® |
| MAJORIS ET460 - 8487 | AD majoris | PP, Unspecified | MAJORIS |