Zytel® HTN 54G35HSLR BK031
| Category: | PPA , HIGH PERFORMANCE POLYAMIDE RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® HTN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SoRwqP_Zytel-HTN-54G35HSLR-BK031.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 35% Glass Reinforced, Toughened, PPA, High Performance Polyamide |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Part Marking Code (SAE J1344) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.42 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.50 | -- | % | |
| Flow | 0.20 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10500 | 10800 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 180 | 166 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 2.7 | % | ISO 527-2 |
| Flexural Modulus | 9300 | 9500 | MPa | ISO 178 |
| Flexural Stress | 280 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 9.0 | 9.0 | kJ/m² | |
| -30°C | 10 | 9.0 | kJ/m² | |
| 23°C | 12 | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -40°C | 75 | 65 | kJ/m² | |
| 23°C | 85 | 70 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 12 | -- | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 283 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 255 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 300 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.0E-5 | -- | cm/cm/°C | |
| Flow : -40 to 23°C | 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 6.8E-5 | -- | cm/cm/°C | |
| Transverse : -40 to 23°C | 6.5E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 43 | 42 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- |
| Note Message | |
|---|---|
| 1 . | First Heat |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nypol® PA A3 G30 HS UV RH AMLA144 NR450 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Caltex PP MT42 | GS Caltex | PP, Unspecified | Caltex PP |
| CABELEC® CC6057 | Cabot Corporation | PP Copolymer | CABELEC® |
| Polifor® 12 T/40 BIANCO 0025 | SO.F.TER. SPA | PP Homopolymer | Polifor® |
| LNP™ THERMOCOMP™ RX06421S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |