Andur 8000 AP/Curene® 442
| Category: | PUR-Ether/TDI , Polyurethane (Polyether, TDI) |
| Manufacturer: | Anderson Development Company |
| Trademark: | Andur |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | So5dgT_Andur-8000-AP-Curene-442.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Andur 8000 AP is a polyether (PPG) based liquid, toluene diisocyanate terminated prepolymer. An elastomer with a hardness of 80 Shore A is obtained when this prepolymer is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be obtained by curing Andur 8000-AP with polyols and their combination with Curene 442 and other diamines, or through the use of plasticizers. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ASTM D1505 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength | ASTM D695 | ||
| 5% strain | 0.421 | MPa | ASTM D695 |
| 10% strain | 1.10 | MPa | ASTM D695 |
| 15% strain | 1.94 | MPa | ASTM D695 |
| 25% strain | 3.17 | MPa | ASTM D695 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 3.76 | MPa | ASTM D412 |
| 300% strain | 7.96 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 14.8 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 420 | % | ASTM D412 |
| Compression Set | 34 | % | ASTM D395B |
| Bayshore Resilience | 20 | % | ASTM D2632 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 10 - 12 | min | |
| Demold Time (100°C) | 40 | min | |
| Post Cure Time (96°C) | 16 | hr |
| Additional Information |
|---|
| Durometer Hardness, ASTM D2240, Shore A: 78 to 82Die C Tear, ASTM D1004: 205 pliAverage Split Tear, ASTM D1938: 55 pliStoichiometry Curative Level: 95%Mix Temperature: Andur 8000 AP: 180-212°F Curene 442: 235-250°F |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 104 - 113 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT4900-611UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Eltex® P KV409 | INEOS Olefins & Polymers Europe | PP Random Copolymer | Eltex® P |
| Hylon® N1013THLUV2 | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| PermaStat® 600.5 | RTP Company | ABS | PermaStat® |
| POLYfill PP CMX8030 VT | Polykemi AB | PP, Unspecified | POLYfill |