RTP VLF 81309
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SnF1Vz_RTP-VLF-81309.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Long Glass Fiber |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.73 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.10 - 0.20 | % | ASTM D955 |
| Moisture Content | 0.040 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 19300 | MPa | ASTM D638 |
| Tensile Strength | 172 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 1.0 - 2.0 | % | ASTM D638 |
| Flexural Modulus | 18600 | MPa | ASTM D790 |
| Flexural Strength | 256 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 160 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 530 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 266 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 6.0 | hr | |
| Processing (Melt) Temp | 313 - 329 | °C | |
| Mold Temperature | 135 - 177 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Use a reverse barrel profile. To maximize fiber length, the following injection barrel, screw, and tip designs should be followed. L/D ratio 16/1 - 22/1, Compression ratio 2:1, Flight depth 0.200 in (5 mm) minimum, in feed section, Screw diameter 0.65 - 0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 5619 | Chevron Phillips Chemical Company LLC | LDPE | MarFlex® |
| Sinvicomp SRF1807 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Sylvin 8230-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Lupox® SG5152 | LG Chem Ltd. | PBT+PET | Lupox® |
| POLYfill PPH T5020 | Polykemi AB | PP Homopolymer | POLYfill |