Next Nylon 66 Prime Series PGF25-01BL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 66 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Smmg6h_Next-Nylon-66-Prime-Series-PGF25-01BL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA66 Glass Fiber Reinforced FR Blue Compound Product Applications Generally suitable for molding insulating parts for electric devices, connectors, switch units, industrial controls etc Benefits Very good combination Mechanical and Electrical properties |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.38 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.50 | -- | % | |
| Across Flow | 0.90 | -- | % | |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 0.75 | -- | % | |
| Saturation 1 | 5.6 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| M-Scale | 105 | -- | ||
| R-Scale | 120 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9000 | 6500 | MPa | ASTM D638 |
| Tensile Strength | 130 | 105 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | 6.0 | % | ASTM D638 |
| Flexural Modulus | 7500 | 6000 | MPa | ASTM D790 |
| Flexural Strength | 250 | 160 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 78 | 88 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 260 | -- | °C | |
| 1.8 MPa, Unannealed | 250 | -- | °C | |
| Melting Temperature | 262 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 25 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | > 375 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | -- | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.60 mm) | 725 | -- | °C | IEC 60695-2-13 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 270 to 280 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 301 TFE 15 FR L | RTP Company | PC | RTP |
| Sumikon® FM-MK201 | Sumitomo Bakelite Co., Ltd. | PPS | Sumikon® |
| Ethavin™ C85FRNC | Vi-Chem Corporation | TPO (POE) | Ethavin™ |
| EPO-TEK® 310M-1 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| INELEC ABSASFR | Infinity LTL Engineered Compounds | ABS | INELEC |