IROGRAN® A 85 P 5350
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | IROGRAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SkwRz0_IROGRAN-A-85-P-5350.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
IROGRAN A 85 P 5350 is a flame-retardant, halogen-free, polyether based thermoplastic polyurethane intended for extrusion and injection moulding applications. IROGRAN A 85 P 5350 is part of the HUNTSMAN technical extrusion product range and offers a specially designed, flexible material with a broad processing window particularly suitable for the preparation of cable jacketing where enhanced fire retardency is required. PERFORMANCE FEATURES
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.17 | g/cm³ | ASTM D792, DIN 53479 |
| Melt Volume-Flow Rate (MVR) (190°C/21.6 kg) | 36.0 | cm³/10min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, DIN 53505 | ||
| Shore A, Injection Molded | 89 | ||
| Shore D, Injection Molded | 37 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion 2 | 40 | mm³ | DIN 53516 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 3 | |||
| 100% Strain | 7.10 | MPa | ASTM D412 |
| 100% Strain | 7.80 | MPa | DIN 53504 |
| 300% Strain | 10.9 | MPa | ASTM D412 |
| 300% Strain | 11.3 | MPa | DIN 53504 |
| Tensile Strength 4 | |||
| Break | 33.1 | MPa | ASTM D412 |
| Break | 45.0 | MPa | DIN 53504 |
| Tensile Elongation 5 | |||
| Break | 750 | % | ASTM D412 |
| Break | 690 | % | DIN 53504 |
| Tear Strength 6 | |||
| -- | 99.8 | kN/m | ASTM D624 |
| -- | 55 | kN/m | ISO 34-1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 7 | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 to 120 | °C | |
| Hot Air Dryer | 60.0 to 80.0 | °C | |
| Drying Time | |||
| -- | 3.0 | hr | |
| Hot Air Dryer | 3.0 | hr | |
| Dew Point | -30.0 | °C | |
| Rear Temperature | 170 to 210 | °C | |
| Middle Temperature | 170 to 210 | °C | |
| Front Temperature | 170 to 210 | °C | |
| Nozzle Temperature | 200 to 210 | °C | |
| Processing (Melt) Temp | 190 to 205 | °C | |
| Mold Temperature | 20.0 to 70.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 3.0 | hr | |
| Hopper Temperature | 25.0 to 40.0 | °C | |
| Cylinder Zone 1 Temp. | 160 to 200 | °C | |
| Cylinder Zone 2 Temp. | 160 to 200 | °C | |
| Cylinder Zone 3 Temp. | 160 to 200 | °C | |
| Cylinder Zone 4 Temp. | 160 to 200 | °C | |
| Cylinder Zone 5 Temp. | 160 to 200 | °C | |
| Adapter Temperature | 175 to 200 | °C | |
| Die Temperature | 175 to 205 | °C |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Injection Molded |
| 3 . | Injection Molded |
| 4 . | Injection Molded |
| 5 . | Injection Molded |
| 6 . | Injection Molded |
| 7 . | Internal testing |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Viprene™ G55A-32U-BLK | Alliance Polymers & Services | TPV | Viprene™ |
| Ateva® 2842AC | Celanese EVA Performance Polymers | EVA | Ateva® |
| Flontech® FLON-5110 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| LNP™ STAT-KON™ DD200C compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ STAT-KON™ |
| LNP™ LUBRICOMP™ RFL36SXS compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |