Alathon® XL3805
| Category: | MDPE , Medium Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SkhGOB_Alathon-XL3805.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ALATHON XL 3805 is an experimental, high molecular weight, medium density polyethylene copolymer with a broad and bimodal mo lecular weight distribution. Films produced from this resin exhibit excellent MD and TD tear with a soft feel and improved optics in a HMW resin. Applications include typical thinner gauge (<1.0 mil.) merchandise bags, grocery sacks, can liners, and produce bags as well as thicker gauge (>1.0 mil.) heavy duty shipping sacks, construction film and agriculture film. This resin can be used to produce mono- and multi-layer films requiring toughness as well as improved feel and appearance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.938 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.057 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| MD : 13 µm | 641 | MPa | ASTM D882 |
| TD : 13 µm | 772 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 13 µm | 26.3 | MPa | ASTM D882 |
| TD : Yield, 13 µm | 23.1 | MPa | ASTM D882 |
| MD : Broken, 13 µm | 88.3 | MPa | ASTM D882 |
| TD : Broken, 13 µm | 47.5 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 13 µm | 270 | % | ASTM D882 |
| TD : Broken, 13 µm | 390 | % | ASTM D882 |
| Total Energy Impact | ASTM D4272 | ||
| 13 µm | 3.12 | J | ASTM D4272 |
| 100 µm | 5.97 | J | ASTM D4272 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 13 µm | 20 | g | ASTM D1922 |
| MD : 100 µm | 420 | g | ASTM D1922 |
| TD : 13 µm | 40 | g | ASTM D1922 |
| TD : 100 µm | 750 | g | ASTM D1922 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 199 - 210 | °C |
| Extrusion instructions |
|---|
| Typical Extrusion ConditionsBlow Up Ratio: 4:1Neck Height: 8 Die Diameters |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4281 | RTP Company | PI, TP | RTP |
| FHR Polypropylene P9M6K-041A | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| Karina BLACK PVC COMPOUND 900-DA-48/ 1-C-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LOXIM 841 02T HB | LOXIM Industries Private Limited | PP Copolymer | LOXIM |
| Eleme NGC400I | Eleme Petrochemical Company Ltd | PP Impact Copolymer | Eleme |