| Lustran SMA 2316 is a 16% glass-reinforced molding grade of impact-modified SMA (styrene/maleic anhydride) terpolymer offering an exceptional balance of processability and performance. Lustran SMA 2316 has high heat resistance coupled with rigidity and decorability, making it an ideal choice for automotive instrument panel and console applications. As with any product, use of Lustran SMA 2316 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 3.3 | g/10 min | |
| Molding Shrinkage | ISO 2577 | ||
| Vertical flow direction | 0.035 | % | ISO 2577 |
| Flow direction | 0.028 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 5500 | MPa | ASTM D638 |
| 23°C | 5780 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield | 77.8 | MPa | ASTM D638 |
| Yield, -30°C | 90.1 | MPa | ISO 527-2 |
| Yield, 23°C | 83.6 | MPa | ISO 527-2 |
| Yield, 85°C | 65.4 | MPa | ISO 527-2 |
| Yield, 107°C | 56.2 | MPa | ISO 527-2 |
| Fracture, 23°C | 84.7 | MPa | ISO 527-2 |
| Flexural Modulus | |||
| -- | 4390 | MPa | ASTM D790 |
| -- | 5290 | MPa | ISO 178 |
| Flexural Stress | |||
| -- 1 | 129 | MPa | ISO 178 |
| Yield | 124 | MPa | ASTM D790 |
| Poisson's Ratio 2 | 0.41 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.7 | kJ/m² | ISO 179/1eA |
| 23°C | 11 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C, 3.18 mm 3 | 69 | J/m | ASTM D256 |
| 23°C, 3.18 mm 4 | 85 | J/m | ASTM D256 |
| -40°C 5 | 8.1 | kJ/m² | ISO 180/1A |
| 23°C 6 | 9.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.18mm 7 | 128 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm span | 129 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 3.18mm 8 | 103 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 4.00mm span | 121 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 141 | °C | ASTM D1525 9 |
| -- | 126 | °C | ISO 306/B50 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 4.1E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 4.7E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 29 | mm/min | SAE J369 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.0 - 93.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Suggested Shot Size | 50 - 75 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 240 - 255 | °C | |
| Middle Temperature | 245 - 260 | °C | |
| Front Temperature | 250 - 265 | °C | |
| Nozzle Temperature | 250 - 265 | °C | |
| Processing (Melt) Temp | 250 - 265 | °C | |
| Mold Temperature | 60.0 - 85.0 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.172 - 0.345 | MPa | |
| Clamp Tonnage | 2.8 - 5.5 | kN/cm² | |
| Cushion | 3.18 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Injection instructions |
|---|
| Screw Speed: ModerateInlet Air Dew Point: -20°F |
| Note Message | |
|---|---|
| 1 . | Yield |
| 2 . | Across Flow: 0.39 |
| 3 . | 0.5x0.125 in |
| 4 . | 0.5x0.125 in |
| 5 . | 4x10 mm |
| 6 . | 4x10 mm |
| 7 . | 0.5x0.125 in |
| 8 . | 0.5x0.125 in |
| 9 . | 标准 B (120°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starflam PX06009 | Eurostar Engineering Plastics | Nylon 6 | Starflam |
| Thermylene® P7-40FG-1804 | Asahi Kasei Plastics North America Inc. | PP, Unspecified | Thermylene® |
| Trademark PE mLLD1918F | Trademark Plastics Corporation | mLLDPE | Trademark PE |
| UNITEM® Rg-30 | Nytef Plastics, Ltd. | PEI | UNITEM® |
| HIPLEX® HHM 5202 | HIP-PetroHemija | HDPE | HIPLEX® |