InnoGreen® BIO-30A
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoGreen® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SkTl58_InnoGreen-BIO-30A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| lnnoGreen® BIO-30A is a 30 shore A polyurethane elastomer formulated for hand-batch and vacuum assisted processing. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. lnnoGreen® BIO-30A contains biobased products. lnnoGreen® Bio-30A has been approved by the USDA as a bio preferred product. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.00 | g/cm³ | |
| Cured | 1.07 | g/cm³ | |
| Base Resin | 1.20 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 to 0.50 | % | ASTM D2566 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 29 Mix Ratio by Volume: 24 | ||
| Demold Time | 480 to 960 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Biobased Content | 38 | % |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.60 | Pa·s | |
| 25°C 2 | 1.3 | Pa·s | |
| 25°C 3 | 4.5 | Pa·s | |
| Curing Time 4 | 40 | hr | |
| Gel Time | 15 to 20 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 25 to 35 | ASTM D2240 | |
| Tensile Strength | 1.14 | MPa | ASTM D638 |
| Tensile Elongation at Break | 100 | % | ASTM D638 |
| Tear Strength | 3.50 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Mixed |
| 3 . | Resin |
| 4 . | 24 hours at 77°F + 16 hours at 150°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PureTherm® 1003C | Tekni-Films, a div of Tekni-Plex | Film, PVC | PureTherm® |
| Bluestar Epoxy JF-46 | Bluestar New Chemical Materials Co. Ltd | Epoxy | Bluestar Epoxy |
| CYCOLOY™ XCM851 resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |
| PERCOM® KCG20B | A. Schulman Europe | PP Copolymer | PERCOM® |
| Plasmer 8165N/1002 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |