Lucon® CP6092
| Category: | PC , Polycarbonate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lucon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SkMHEu_LuconCP6092.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Electrostatic Dissipation (1.0E+07 ~ 1.0E+10 ohm) High Impact Strength Application ATM parts |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/2.16 kg) | 16 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 - 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 93.2 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 6.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 4710 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 147 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 170 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 137 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+7 - 1.0E+10 | ohms | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70 - 80 | °C | |
| Drying Time | 5.0 - 7.0 | hr | |
| Rear Temperature | 280 - 290 | °C | |
| Middle Temperature | 290 - 300 | °C | |
| Front Temperature | 290 - 310 | °C | |
| Nozzle Temperature | 290 - 310 | °C | |
| Processing (Melt) Temp | 290 - 310 | °C | |
| Mold Temperature | 80 - 100 | °C | |
| Back Pressure | 0.00 - 0.981 | MPa | |
| Screw Speed | 40 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC V143-70E | Vi-Chem Corporation | PVC, Flexible | Vi-Chem PVC |
| Celcon® MR90B | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| LUBEMID B27 GF50 NATURAL | LUBEN PLAST srl | Nylon 6 | LUBEMID |
| Pinnacle PP 1112 Z | Pinnacle Polymers | PP Homopolymer | Pinnacle PP |
| POLYfill PPC GF5020 | Polykemi AB | PP Copolymer | POLYfill |