VALOX™ 357X resin
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Sifxy4_VALOX-357X-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VALOX 357X is an impact modified, flame retarted PBT+PC blend. Applications like bobbins, switches and enclosures. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 250°C/5.0 kg | 9.6 | g/10 min | |
| 265°C/5.0 kg | 13 | g/10 min | |
| 266°C/5.0 kg | 13 | g/10 min | |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 250°C/5.0 kg | 8.00 | cm³/10min | |
| 265°C/5.0 kg | 10.0 | cm³/10min | |
| Molding Shrinkage | Internal Method | ||
| Flow 1 | 1.1 to 1.8 | % | |
| Flow : 3.20 mm | 1.0 to 1.4 | % | |
| Across Flow 2 | 0.90 to 1.8 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.50 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 115 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 3 | 2000 | MPa | ASTM D638 |
| -- | 2200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 4 | 50.0 | MPa | ASTM D638 |
| Yield | 50.0 | MPa | ISO 527-2/50 |
| Break 5 | 40.0 | MPa | ASTM D638 |
| Break | 40.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 6 | 5.0 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2/50 |
| Break 7 | 30 | % | ASTM D638 |
| Break | 30 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 8 | 2100 | MPa | ASTM D790 |
| -- 9 | 2000 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 80.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 10 | 78.0 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 33.0 | mg | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C 11 | 20 | kJ/m² | ISO 179/1eA, ISO 179/2C |
| 23°C 12 | 45 | kJ/m² | ISO 179/1eA |
| 23°C | 40 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength 13 | ISO 179/1eU, ISO 179/2U | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| -30°C | 150 | J/m | ASTM D256 |
| 0°C | 190 | J/m | ASTM D256 |
| 23°C | 500 | J/m | ASTM D256 |
| -30°C 14 | 10 | kJ/m² | ISO 180/1A |
| 0°C 15 | 20 | kJ/m² | ISO 180/1A |
| 23°C 16 | 40 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | ASTM D4812, ISO 180/1U | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Instrumented Dart Impact (23°C, Total Energy) | 35.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 130 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 100 mm Span 17 | 135 | °C | ISO 75-2/Be |
| 0.45 MPa, Unannealed, 64.0 mm Span 18 | 130 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 85.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 19 | 85.0 | °C | ISO 75-2/Ae |
| 1.8 MPa, Unannealed, 64.0 mm Span 20 | 85.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 180 | °C | ASTM D1525, ISO 306/A50 13 21 |
| -- | 145 | °C | ASTM D1525, ISO 306/B50 14 22 |
| -- | 150 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -40 to 40°C | 9.2E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 8.4E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 80°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.17 | W/m/K | ISO 8302 |
| RTI Elec | 120 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI Str | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | |||
| 1.60 mm, in Oil | 25 | kV/mm | ASTM D149, IEC 60243-1 |
| 3.20 mm, in Oil | 17 | kV/mm | ASTM D149, IEC 60243-1 |
| 0.800 mm, in Oil | 34 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 1 MHz | 3.00 | ASTM D150, IEC 60250 | |
| 50 Hz | 3.00 | IEC 60250 | |
| 60 Hz | 3.00 | IEC 60250 | |
| Dissipation Factor | |||
| 1 MHz | 0.013 | ASTM D150 | |
| 50 Hz | 2.0E-3 | IEC 60250 | |
| 60 Hz | 2.0E-3 | IEC 60250 | |
| 1 MHz | 1.3E-3 | IEC 60250 | |
| Arc Resistance 23 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| Comparative Tracking Index | IEC 60112 | ||
| -- | 225 | V | |
| Solution B | 100 | V | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 2.50 mm | 5VA | ||
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 30 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (260°C, 1500 sec^-1) | 310 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Rear Temperature | 230 to 245 | °C | |
| Middle Temperature | 240 to 255 | °C | |
| Front Temperature | 245 to 265 | °C | |
| Nozzle Temperature | 240 to 260 | °C | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 40.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | Tensile Bar |
| 3 . | 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | Type I, 50 mm/min |
| 7 . | Type I, 50 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | 1.3 mm/min |
| 11 . | 80*10*4 sp=62mm |
| 12 . | 80*10*4 sp=62mm |
| 13 . | 80*10*4 sp=62mm |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 |
| 16 . | 80*10*4 |
| 17 . | 120*10*4 mm |
| 18 . | 80*10*4 mm |
| 19 . | 120*10*4 mm |
| 20 . | 80*10*4 mm |
| 21 . | Rate A (50°C/h), Loading 2 (50 N) |
| 22 . | Rate B (120°C/h), Loading 2 (50 N) |
| 23 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene M25P251-01A | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| ExxonMobil™ HDPE HMA 025 | ExxonMobil Chemical | HDPE, UHMW | ExxonMobil™ HDPE |
| Hifax TYC 773P | LyondellBasell Industries | TPO (POE) | Hifax |
| Hostacom BA742EC | LyondellBasell Industries | PP Copolymer | Hostacom |
| HydroThane™ AL 93A (Hydrated) | AdvanSource Biomaterials Corp. | TPU, Unspecified | HydroThane™ |