Latamid 66 H2 G/50-GWHF1
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latamid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SiNmsi_Latamid-66-H2-G-50-GWHF1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 66 (PA66) based compound. Heat stabilised. Glass fibres. improved G.W.F.I. compared to standard product. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.58 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.80 to 1.2 | % | |
| Flow : 2.00 mm | 0.30 to 0.60 | % | |
| Water Absorption (23°C, 24 hr) | 0.26 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 16500 | MPa | |
| 60°C | 11000 | MPa | |
| 90°C | 6500 | MPa | |
| 120°C | 6000 | MPa | |
| 150°C | 5000 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 205 | MPa | |
| Break, 60°C | 150 | MPa | |
| Break, 90°C | 110 | MPa | |
| Break, 120°C | 90.0 | MPa | |
| Break, 150°C | 80.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 2.2 | % | |
| Break, 60°C | 3.0 | % | |
| Break, 90°C | 3.8 | % | |
| Break, 120°C | 4.1 | % | |
| Break, 150°C | 4.4 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 65 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 260 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 135 | °C | |
| Vicat Softening Temperature | 255 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 4.0E-6 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 800 | °C | |
| 2.00 mm | 800 | °C | |
| Oxygen Index | 27 | % | ASTM D2863 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Dimensional Stability | 51.0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 70.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TUFNYL® SXXIC C NATURAL | SRF Ltd. | Nylon 6 | TUFNYL® |
| DURACON® M90-45 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| Hapflex™ 669-3 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| Plaslube® PA4/6 CF30 TL15 | Techmer Engineered Solutions | Nylon 46 | Plaslube® |
| Sylvin 8215-82 Purple 8424 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |