EPOXIDUR® EP 3585
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | RASCHIG GmbH |
| Trademark: | EPOXIDUR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Si0prG_EPOXIDUR-EP-3585.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Glass-fibre reinforced and inorganically filled epoxy moulding compound Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures, excellent cracking resistance regarding thermal shock stress Rotors, magnetic coil coatings This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.85 to 1.95 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 to 1.00 | g/cm³ | ISO 60 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | < 0.10 | % | ISO 62 |
| Post Shrinkage 1 | < 0.050 | % | ISO 2577 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | > 5.00 | MPa | |
| Compression Molding Temperature | 150 to 190 | °C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15000 to 18000 | MPa | ISO 527-2 |
| Tensile Stress | 100 to 120 | MPa | ISO 527-2 |
| Flexural Modulus | 16000 to 19000 | MPa | ISO 178 |
| Flexural Stress | 190 to 210 | MPa | ISO 178 |
| Compressive Stress | 200 to 220 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 to 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 15 to 18 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | > 200 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 150 to 170 | °C | ISO 75-2/C |
| CLTE - Flow (50 to 150°C) | 1.5E-5 to 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.40 to 0.60 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 to 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 to 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | 20 to 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 6.00 4.00 | ||
| 1 MHz | 6.00 4.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.010 to 0.020 | ||
| 1 MHz | 0.020 to 0.040 | ||
| Arc Resistance | PLC 4 | ASTM D495 | |
| Comparative Tracking Index | > 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index | 900 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 900 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Middle Temperature | 50.0 to 70.0 | °C | |
| Front Temperature | 70.0 to 90.0 | °C | |
| Processing (Melt) Temp | 90.0 to 105 | °C | |
| Mold Temperature | 150 to 190 | °C | |
| Back Pressure | 0.500 to 1.50 | MPa | |
| Screw Speed | 40 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | 168 h / 110°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8476-90UV Red 6257 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ALFATER XL® A85E 2GP0000 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |
| LNP™ THERMOCOMP™ RZ006 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Sylvin 8225-90FU Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 9077-60 Grey 930 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |