Badamid® B80
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ShXWRb_Badamid-B80.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Suitable for extrusion and injection moulding with a well-balanced ratio of mechanical properties and processability |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 9.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 3.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3000 | 1300 | MPa | ISO 527-2/1 |
| Tensile Stress 1(Yield, 23°C) | 80.0 | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain 2(Yield, 23°C) | 4.5 | 20 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break 3(23°C) | 30 | > 50 | % | ISO 527-2/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength 4 | ISO 179/1eA | |||
| -30°C | 9.0 | -- | kJ/m² | |
| 23°C | 10 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength 5 | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break | ||
| Notched Izod Impact Strength 6 | ISO 180/1A | |||
| -30°C | 8.0 | -- | kJ/m² | |
| 23°C | 9.0 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 7 | ||||
| 0.45 MPa, Unannealed | 180 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 8 | 222 | -- | °C | ISO 3146 |
| CLTE - Flow 9 | 8.5E-5 | -- | cm/cm/°C | DIN 53752 |
| Maximum Service Temperature | IEC 216 | |||
| 20000 hrs | 70 | -- | °C | |
| some hours | 180 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity 10 | 1.0E+13 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity 11 | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength 12 | 100 | 60 | kV/mm | IEC 60243-1 |
| Relative Permittivity 13 | 3.50 | 7.00 | IEC 60250 | |
| Dissipation Factor | 0.030 | 0.30 | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm 14 | V-2 | -- | ||
| 1.60 mm 15 | V-2 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | Test Specimen accordng to ISO 3167, Type A |
| 4 . | 80x10x4 mm |
| 5 . | 80x10x4 mm |
| 6 . | 80x10x4 mm |
| 7 . | 110x10x4 mm |
| 8 . | 10 K/min, Compound for moulding |
| 9 . | >=10x10x4 mm |
| 10 . | 80x80x1 mm |
| 11 . | 80x80x1 mm |
| 12 . | 80x80x1 mm |
| 13 . | 80x80x1 mm |
| 14 . | 125x13x0.8 mm |
| 15 . | 125x13x1.6 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimoFlo 70A-300 | KMI Group Inc. | SEBS | PrimoFlo |
| TIPPLEN® K 499 | MOL Petrochemicals Co. Ltd. | PP Impact Copolymer | TIPPLEN® |
| CERTENE™ PBM-35 | Muehlstein | PP Impact Copolymer | CERTENE™ |
| Kotex K-20UV28 | Kotec Corporation | PC | Kotex |
| Sylvin 8240-75 Grey 9576 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |