Generic TPU-Polyester - Glass Fiber
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ShWiFg_Generic-TPU-Polyester---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic TPU-Polyester - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 - 1.55 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C) | 0.10 - 0.50 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.14 - 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (23°C) | 64 - 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 345 - 3470 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 14.5 - 29.0 | MPa | ASTM D638 |
| 23°C | 17.2 - 83.2 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 10 - 11 | % | ASTM D638 |
| Fracture, 23°C | 3.2 - 13 | % | ASTM D638 |
| Flexural Modulus (23°C) | 276 - 7070 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 9.65 - 211 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 62 - 800 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1300 - 1600 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 54.0 - 127 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 54.4 - 83.6 | °C | ASTM D648 |
| CLTE - Flow | 1.3E-6 - 1.3E-4 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity (23°C) | 0.36 - 0.41 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+11 - 2.5E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 18 - 20 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C) | 3.67 - 4.83 | ASTM D150 | |
| Dissipation Factor (23°C) | 0.012 - 0.014 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 107 | °C | |
| Drying Time | 3.5 - 6.0 | hr | |
| Rear Temperature | 195 - 197 | °C | |
| Middle Temperature | 196 - 197 | °C | |
| Front Temperature | 196 - 197 | °C | |
| Processing (Melt) Temp | 202 - 235 | °C | |
| Mold Temperature | 39.7 - 72.5 | °C | |
| Injection Pressure | 85.8 - 86.9 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic TPU-Polyester - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MALECCA K-090 | Denka Company Limited | ABS | MALECCA |
| SLOVAMID® 6 GF 60 000/1M | Plastcom | Nylon 6 | SLOVAMID® 6 |
| BJB Polyurethane TC-886 FR REV 1 | BJB Enterprises, Inc. | PUR, Unspecified | BJB Polyurethane |
| Cardia Biohybrid™ H-FM | Cardia Bioplastics™ | TPS+PP | Cardia Biohybrid™ |
| Sylvin 9067-80 Orange 596 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |