Polytron® P30B01
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | Polytron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ShSeuY_Polytron-P30B01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A chemically coupled 30% LGF reinforced black PP, heat stabilized for high temperature applications such as under the hood automotive parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.17 | % | ASTM D955 |
| -- | 0.17 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6250 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 110 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 2.2 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 6450 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 160 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 16 | kJ/m² | |
| 23°C | 17 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 45 | kJ/m² | |
| 23°C | 55 | kJ/m² | |
| Notched Izod Impact | |||
| 23°C | 170 | J/m | ASTM D256 |
| 23°C | 18 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 157 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 167 | °C | ISO 11357-3, ASTM D3418 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 | |
| Glow Wire Flammability Index | 750 | °C | IEC 60695-2-12 |
| Flammability | 30 | mm/min | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN AG10NP | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| Mirakutoran® TPU E885 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Mylar® EL (92 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Advanced Composites ADX-5001 | Advanced Composites, Inc. | PP, Unspecified | Advanced Composites |
| AT 220 | Celanese EVA Performance Polymers | LDPE | AT |