LEXAN™ FST9405T resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ShPLEk_LEXANFST9405Tresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lexan* FST9405T resin is a high flow PC Copolymer Resin, suitable for injection molding. This halogen-free flame retardant resin is OSU55/55 and FAR25.583 compliant and an ideal candidate for aircraft interior applications. Available in opaque colors. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 9.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow | 0.50 - 0.70 | % | Internal method |
| Transverse flow | 0.50 - 0.70 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2600 | MPa | ASTM D638 |
| -- | 2600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 77.0 | MPa | ASTM D638 |
| Yield | 77.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 70.0 | MPa | ASTM D638 |
| Fracture | 70.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Fracture 5 | 75 | % | ASTM D638 |
| Fracture | 95 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2700 | MPa | ASTM D790 |
| -- 7 | 2500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 105 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 115 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | No Break | ISO 179/1eA | |
| 23°C | No Break | ISO 179/1eA | |
| Charpy Unnotched Impact Strength 10 | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -30°C | 85 | J/m | ASTM D256 |
| 23°C | 130 | J/m | ASTM D256 |
| -30°C 11 | 9.0 | kJ/m² | ISO 180/1A |
| 23°C 12 | 11 | kJ/m² | ISO 180/1A |
| 23°C 13 | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 14 | ISO 180/1U | ||
| -30°C | No Break | ISO 180/1U | |
| 23°C | No Break | ISO 180/1U | |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 60.0 | J | ASTM D3763 |
| -- | 130 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 105 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 15 | 94.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 95.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 16 | 104 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 114 | °C | ASTM D1525 17 |
| -- | 113 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : -40 to 40°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| NBS Smoke Density - Flaming, Dmax | ASTM E662 | ||
| OSU peak heat release rate 18 | kW/m² | FAR 25.853 | |
| OSU total heat release 19 | kW·min/m² | FAR 25.853 | |
| Vertical Burn Test - Test a (60 s), passes at | 1.0 | sec | FAR 25.853 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95 - 100 | °C | |
| Drying Time | 6.0 - 8.0 | hr | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 230 - 250 | °C | |
| Middle Temperature | 240 - 270 | °C | |
| Front Temperature | 250 - 280 | °C | |
| Nozzle Temperature | 245 - 275 | °C | |
| Processing (Melt) Temp | 250 - 280 | °C | |
| Mold Temperature | 50 - 80 | °C | |
| Back Pressure | 0.300 - 0.700 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 sp=62mm |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*3 |
| 14 . | 80*10*3 |
| 15 . | 80*10*4 mm |
| 16 . | 80*10*4 mm |
| 17 . | 标准 B (120°C/h), 载荷2 (50N) |
| 18 . | 5 minute test |
| 19 . | 2 minute test |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNIFLEX® VA7400 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PCTFE | TEKNIFLEX® |
| NORYL™ LEN2211 resin | SABIC Innovative Plastics Asia Pacific | PPE+PS | NORYL™ |
| Kotex K-20UVR28 | Kotec Corporation | PC | Kotex |
| SABIC® PPcompound 31T1010 | Saudi Basic Industries Corporation (SABIC) | PP Impact Copolymer | SABIC® PPcompound |
| LEXAN™ LUX7632C resin | SABIC Innovative Plastics | PC | LEXAN™ |