DOW™ HDPE 90052L
| Category: | HDPE , High Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ShA2z2_DOW-HDPE-90052L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOW™ HDPE 90052L is a High Density Polyethylene Resin material. It is available in Latin America. Important attributes of DOW™ HDPE 90052L are:
Typical application of DOW™ HDPE 90052L: Food Contact Applications |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.952 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/21.6 kg | 11 | g/10 min | |
| 190°C/5.0 kg | 0.35 | g/10 min |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 15 | µm | |
| Film Puncture Resistance (15 µm) | 5.00 | J/cm³ | ASTM D5748 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 15 µm | 33.0 | MPa | |
| TD : Yield, 15 µm | 30.0 | MPa | |
| MD : Break, 15 µm | 78.0 | MPa | |
| TD : Break, 15 µm | 44.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 15 µm | 530 | % | |
| TD : Break, 15 µm | 610 | % | |
| Dart Drop Impact (15 µm) | 140 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 15 µm | 9.0 | g | |
| TD : 15 µm | 110 | g |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 211 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M1170 FR | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| KumhoSunny PC 2500FR | Shanghai KumhoSunny Plastics Co., Ltd. | PC | KumhoSunny PC |
| Iupiace® GV30 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| LG ABS SG175G | LG Chem Ltd. | ABS | LG ABS |
| MAJORIS EB710 | AD majoris | PP, Unspecified | MAJORIS |