ACCUCOMP™ HP0306L
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Sgdm5w_ACCUCOMP-HP0306L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUCOMP™ HP0306L is a Polypropylene Homopolymer (PP Homopolymer) product. It is available in North America. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.901 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.2 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 92 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1300 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 36.0 | MPa | |
| Break | 22.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 10 | % | |
| Break | 400 | % | |
| Flexural Modulus | 1400 | MPa | ASTM D790 |
| Flexural Strength | 42.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 30 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 82.0 | °C | |
| 1.8 MPa, Unannealed | 53.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G30 211 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| SCHULAMID® 612 FS 5003 MC | A. Schulman Europe | Nylon 612 | SCHULAMID® |
| NuSil R-2160 | NuSil Technology | Silicone | NuSil |
| DynaMix™ XP-5539 | Polymer Dynamix | TP, Unspecified | DynaMix™ |
| INNOPOL® PP CS 2-8960 | Inno-Comp Ltd. | PP Copolymer | INNOPOL® PP |