| LNP STAT-KON EX12310C is an Electrical Conductive thermoplastic compound featuring Electrostatic Discharge (ESD) Safe performance based on a unique Ultra Clean Polyetherimide resin reinforced with 10% carbon fiber. This compound provides good stiffness, dimension stability and has extremely high level of cleanliness for the most demanding applications in the Hard Disk Drive and Semiconductor Industry. A unique feature of this material is its low C18-C40 hydrocarbons and this compound is manufactured using the LNP Clean Compounding Solution (CCS) Technology. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.31 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (367°C/6.6 kg) | 31 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.40 | % | |
| Across Flow : 24 hr | 0.50 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 9170 | MPa | ASTM D638 |
| -- | 8980 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 3 | 158 | MPa | ASTM D638 |
| Break | 156 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 4 | 2.4 | % | ASTM D638 |
| Break | 2.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 5 | 8140 | MPa | ASTM D790 |
| -- 6 | 8410 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 225 | MPa | ISO 178 |
| Break, 50.0 mm Span 7 | 224 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 8(23°C) | 3.6 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 32 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 197 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 201 | °C | ISO 75-2/Af |
| CLTE | ASTM E831 | ||
| Flow : 40 to 120°C | 1.6E-5 | cm/cm/°C | |
| Transverse : 40 to 120°C | 6.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 4.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | 5.1E+5 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.600 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 330 to 380 | °C | |
| Middle Temperature | 340 to 380 | °C | |
| Front Temperature | 345 to 380 | °C | |
| Nozzle Temperature | 345 to 380 | °C | |
| Processing (Melt) Temp | 350 to 380 | °C | |
| Mold Temperature | 135 to 165 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Molded |
| 2 . | 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 mm, Cut |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PC-UV1-D(f1)-(color)-1 | Polymer Resources Ltd. | PC | PRL |
| TECHNYL® C R 218 V30 BLACK 1 N | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| Sinvicomp DBS3025 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Aropol™ L 67300 resins | Ashland Performance Materials | Polyester, TS | Aropol™ |
| Latamid 66 | LATI S.p.A. | Nylon 66 | Latamid |