NILAMID® A3 GB30 TF20 is a Polyamide 66 (Nylon 66) compound, 30% glass bead reinforced, low wear and friction with 20% PTFE, UL listed HB. This compound is intended for injection molding. NILAMID® A3 GB30 TF20 is primarily designed for the Industrial and Consumer industry. It is also suitable for Electrical and Electronic or Automotive applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.50 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 23°C | 1.1 | % | |
| Flow : 23°C | 1.1 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.40 | % | |
| Saturation, 23°C | 4.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 4500 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 65.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield, 23°C | 4.0 | % | |
| Break, 23°C | 8.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 3.5 | kJ/m² | |
| 23°C | 4.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| 23°C | 14 | kJ/m² | |
| 30°C | 13 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 3.2 | kJ/m² | |
| 23°C | 4.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 230 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 110 | °C | ISO 75-2/A |
| Continuous Use Temperature 1 | 100 | °C | IEC 60216 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass | ||
| 165°C | Pass |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 2 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 18 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (3.20 mm, Solution A) | 550 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.400 mm, NC | HB | ||
| 0.800 mm | HB | ||
| 1.60 mm, NC | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.800 mm | 650 | °C | |
| 3.20 mm | 650 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.800 mm | 675 | °C | |
| 3.20 mm | 675 | °C | |
| Oxygen Index | 27 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 20000 hr |
| 2 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VENYL SG507 - 8139 | AD majoris | Nylon 6 | VENYL |
| Gravi-Tech™ GT6000-0023 Black | PolyOne Corporation | Nylon 6 | Gravi-Tech™ |
| Hifax TYC 1168X | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |
| Karina COMP. PVC CRYSTAL -E 60/264-D-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lutene® XL8080UCS | LG Chem Ltd. | PE, Unspecified | Lutene® |