Tuftec™ L5201

Category:	SEBS , Styrene Ethylene Butylene Styrene Block Copolymer
Manufacturer:	AKelastomers
Trademark:	Tuftec™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ScRMZM_TuftecL5201.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Asahi Kasei Tuftec™ Trial L521 is particularly designed as a modifier to increase flexibility of polypropylene (PP). Its excellent compatibility makes L521 super-finely dispersed into PP. PP and L521 blends provides transparent and flexible extruded products such as sheets, films and tubes. The blends are also applicable to injection molding due to its high MFR. It has excellent adhesion, which is suitable for the use of adhesive layer of protective films with hot-melt and pressure sensitive characteristics. L521 meets USP Class VI standards. It may be used for medical applications after a special agreement with Asahi Kasei.

Message

Asahi Kasei Tuftec™ Trial L521 is particularly designed as a modifier to increase flexibility of polypropylene (PP). Its excellent compatibility makes L521 super-finely dispersed into PP. PP and L521 blends provides transparent and flexible extruded products such as sheets, films and tubes. The blends are also applicable to injection molding due to its high MFR. It has excellent adhesion, which is suitable for the use of adhesive layer of protective films with hot-melt and pressure sensitive characteristics. L521 meets USP Class VI standards. It may be used for medical applications after a special agreement with Asahi Kasei.

General Information
Features	Good adhesion
Uses	Films Pipe fittings Sheet Plastic modification Medical/nursing supplies
Agency Ratings	USP Class VI
Forms	Particle
Processing Method	Extrusion Injection molding

Physical	Nominal Value	Unit	Test Method
Density	0.890	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR)			ISO 1133
190°C/2.16 kg	2.3	g/10 min	ISO 1133
230°C/2.16 kg	15	g/10 min	ISO 1133

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	39		ISO 7619

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress (300% Strain)	1.30	MPa	ISO 37
Tensile Stress ¹(Break)	12.5	MPa	ISO 37
Tensile Elongation ²(Break)	810	%	ISO 37

Additional Information	Nominal Value		Test Method
Styrene/Rubber ratio	18/82		Internal method

Note Message
1 .	Type 1A, 500mm/min
2 .	Type 1A, 500mm/min

Resin Grade	Manufacturer	Category	Trademark
SNOLEN® EP 0.26/51 Y	JSC Gazprom neftekhim Salavat	HDPE	SNOLEN®
Stratasys PC-ABS	Stratasys	PC+ABS	Stratasys
YUPLENE® BX39A	SK Global Chemical	PP Impact Copolymer	YUPLENE®
Karina IVORY PVC COMPOUND 900-35/ 1-AYR-AC-LMP	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
LEXAN™ 241R resin	SABIC Innovative Plastics	PC	LEXAN™