Latilon 30D G/10-V0
| Category: | PC , Polycarbonate |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latilon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SbmT4V_Latilon-30D-G-10-V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polycarbonate (PC). Glass fibres. UL94 V-0 classified, with halogens, PBB/PBDE and antimonium trioxide free. Product UL certified. Low smoke toxicity index and optical density. High dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.26 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.60 to 0.75 | % | |
| Flow : 2.00 mm | 0.45 to 0.65 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 3100 | MPa | |
| 60°C | 2900 | MPa | |
| 90°C | 2800 | MPa | |
| 120°C | 2200 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 60.0 | MPa | |
| Yield, 60°C | 50.0 | MPa | |
| Yield, 90°C | 45.0 | MPa | |
| Yield, 120°C | 30.0 | MPa | |
| Break, 23°C | 45.0 | MPa | |
| Break, 60°C | 25.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 4.0 | % | |
| Yield, 60°C | 3.0 | % | |
| Yield, 90°C | 2.8 | % | |
| Yield, 120°C | 2.2 | % | |
| Break, 23°C | 35 | % | |
| Break, 60°C | 30 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 6.0 | kJ/m² | |
| 23°C | 7.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact (23°C, 3.20 mm) | 90 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 140 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 130 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 130 | °C | |
| Vicat Softening Temperature | 145 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 2.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-2 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 850 | °C | |
| 2.00 mm | 850 | °C | |
| Oxygen Index | 34 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 100 to 120 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nypol® PA B3 HL HV400 NTLA010 NT389 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| DEXFLEX® 940D FP | LyondellBasell Industries | TPO (POE) | DEXFLEX® |
| Jackdaw ABS/PC FX70GY6582 | Jackdaw Polymers | PC+ABS | Jackdaw ABS/PC |
| Karina WHITE PVC COMPOUND 800-10/93-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hostacom EP3307 G12771 | LyondellBasell Industries | PP Copolymer | Hostacom |