Reny® 2620
| Category: | PARA , Polyarylamide |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Reny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Sbd1kk_Reny-2620.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Reny® 2620 is a Polyarylamide (PARA) material filled with 20% glass\mineral. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Reny® 2620 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.66 | -- | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 18 | -- | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 12.3 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.46 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 0.14 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.3 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 17600 | 11500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 139 | 86.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.1 | 1.3 | % | ISO 527-2 |
| Flexural Modulus | 16000 | 10900 | MPa | ISO 178 |
| Flexural Stress | 236 | 151 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.1 | 5.1 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 27 | 35 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 234 | 231 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 214 | 196 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | |||
| Flow | 1.0E-5 | -- | cm/cm/°C | |
| Transverse | 4.0E-5 | -- | cm/cm/°C |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 120 | °C | |
| B | 80.0 | °C | |
| Drying Time | |||
| A | > 3.0 | hr | |
| B | > 12 | hr | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 275 | °C | |
| Front Temperature | 280 | °C | |
| Nozzle Temperature | 280 | °C | |
| Mold Temperature | 120 to 140 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® Homo 120.0 | Marco Polo International, Inc. | PP Homopolymer | MARPOL® Homo |
| Makrolon® SF800 Z MAS148 | Covestro - Polycarbonates | PC | Makrolon® |
| Makrolon® 8325 | Covestro - Polycarbonates | PC | Makrolon® |
| Sevrene® 3090-46D | Vi-Chem Corporation | TPE | Sevrene® |
| Leona™ 1402SH | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |