| Lubricated Medium Viscosity Acetal Homopolymer with Low Wear and Low Friction |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.8 | % | |
| Flow | 1.9 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 2.00 mm | 1.0 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.25 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | ||
| M-Scale | 92 | ||
| R-Scale | 120 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 67.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 15 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 25 | % | ISO 527-2 |
| Flexural Modulus | 2900 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 290 | kJ/m² | |
| 23°C | 350 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 9.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 158 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 160 | °C | ISO 306/B50 |
| Melting Temperature 1 | 178 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.1E-4 | cm/cm/°C | |
| Transverse | 1.1E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 4.20 | ||
| 1 MHz | 4.10 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (1.00 mm) | 28 | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.800 mm | HB | ||
| 1.50 mm | HB |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vitaster® UR36NT6208 | Jackdaw Polymers | PBT | Vitaster® |
| Ultramid® A27 E 01 | BASF Corporation | Nylon 66 | Ultramid® |
| PHOENIX™ 11101 | Phon Tech Industrial Company | SBC | PHOENIX™ |
| Plenco 02567 (Compression) | Plastics Engineering Co. | Phenolic | Plenco |
| ExxonMobil™ HDPE HTA 001HP5 | ExxonMobil Chemical | HDPE, HMW | ExxonMobil™ HDPE |