LNP™ THERMOCOMP™ SF008 compound
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Sa6D8c_LNPTHERMOCOMPSF008compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP SF008 is a compound based on Nylon 12 resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound SF-1008 Product reorder name: SF008 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.20 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.70 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.73 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.18 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8270 | MPa | ASTM D638 |
| -- | 8760 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 136 | MPa | ASTM D638 |
| Fracture | 152 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 11 | % | ASTM D638 |
| Fracture | 9.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 7580 | MPa | ASTM D790 |
| -- | 9000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 96.5 | MPa | ASTM D790 |
| -- | 213 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 260 | J/m | ASTM D256 |
| 23°C 2 | 18 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1400 | J/m | ASTM D4812 |
| 23°C 3 | 76 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 177 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 170 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 166 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 - 0.20 | % | |
| Rear Temperature | 216 - 227 | °C | |
| Middle Temperature | 221 - 232 | °C | |
| Front Temperature | 227 - 238 | °C | |
| Processing (Melt) Temp | 227 - 238 | °C | |
| Mold Temperature | 71.1 - 82.2 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radiflam® S RV300K AE 121 C NAT 3702 | Radici Plastics | Nylon 6 | Radiflam® |
| Sympoxy™ 1225/803 | Hapco Inc. | Epoxy | Sympoxy™ |
| APEX® 84217 | Teknor Apex Company | PVC, Flexible | APEX® |
| COSMOPLENE® AW564 | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP Copolymer | COSMOPLENE® |
| DOW™ Electrical & Telecommunications DGDK-6862 NT | The Dow Chemical Company | HDPE | DOW™ Electrical & Telecommunications |