Devcon FasMetal™ 10 HVAC Repair

Category:	Epoxy , Epoxy; Epoxide
Manufacturer:	Devcon
Trademark:	Devcon
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Sa07N0_Devcon-FasMetal-10-HVAC-Repair.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

An aluminum-filled, 1:1 mix epoxy packaged in 6 1/2 oz. tube kit for repairs to copper coils in HVAC equipment.

Intended Use:

Seal leaks in pipes and tanks; repair copper coils in compressors; repair holes in aluminum and other metals

Product Features:

Fills voids or pores in castings

Bonds, patches, and seals metals

Good stability in Freon Environment

Bonds to aluminum, concrete, and many other metals

Aids in quickly returning equipment back to service

Hardens to a rigid material that can be ground, drilled, or tapped

General Information
Filler / Reinforcement	Aluminum filler
Features	Rigidity, high Adhesiveness
Uses	Repair Materials Bonding
Appearance	Aluminum white

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.72	g/cm³
Specific Volume	0.582	cm³/g
Solid content- by Volume	100	%

Additional Information	Nominal Value	Unit	Test Method
Temperature Resistance
Dry	121	°C
Wet	43	°C
Tensile Shear Adhesion	17.2	MPa	ASTM D1002

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage - Flow	0.080	%	ASTM D2566

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	85		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	5380	MPa	ASTM D638
Flexural Strength	43.2	MPa	ASTM D790
Compressive Strength	58.1	MPa	ASTM D695

Thermal	Nominal Value	Unit	Test Method
CLTE - Flow	5.2E-5	cm/cm/°C	ASTM D696
Thermal Conductivity	0.72	W/m/K	ASTM C177

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength	3.9	kV/mm	ASTM D149
Dielectric Constant	21.4		ASTM D150

Thermoset	Nominal Value	Unit	Test Method
Thermoset Components
Component a	Mixing ratio by weight: 0.90 Mixing ratio by capacity: 1.0
Component B	Mixing ratio by weight: 1.0 Mixing ratio by capacity: 1.0
Pot Life (24°C)	60	min
Thermoset Mix Viscosity	40000	cP

Additional Information	Nominal Value	Unit	Test Method
Cured 7 days @ 75°F

Uncured Properties	Nominal Value	Unit	Test Method
Curing Time	16	hr

Resin Grade	Manufacturer	Category	Trademark
POLYFORT® FPP 3551EU	A. Schulman Inc.	PP, Unspecified	POLYFORT®
RTP 399 X 115062 F	RTP Company	PC	RTP
INEOS PP 240-HP25	INEOS Olefins & Polymers Europe	PP Random Copolymer	INEOS PP
Jackdaw ABS GX10BL6576	Jackdaw Polymers	ABS	Jackdaw ABS
Jamplast JPGPPSI	Jamplast, Inc.	PS (GPPS)	Jamplast