SABIC® HDPE F04660 (Blow moulding)
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SZNWpT_SABIC-HDPE-F04660-Blow-moulding-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE F04660 is a high density polyethylene blow moulding grade for high rigidity, good toughness and processability. These properties offer bottles to be made at lower weight with good top load strength. Typical applications. SABIC® HDPE F04660 can be used in hollow thinwalled parts and profile extrusions. It is not recommended for packaging environmentally active materials such as soaps, detergents, shampoos, etc. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.961 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.70 | g/10 min | |
| 190°C/21.6 kg | 46 | g/10 min | |
| 190°C/5.0 kg | 3.0 | g/10 min | |
| Environmental Stress-Cracking Resistance (10% Igepal CO-630, Compression Molded, F50) | 15.0 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1250 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00 mm, Compression Molded | 29.0 | MPa | |
| Break, 2.00 mm, Compression Molded | 18.0 | MPa | |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | > 1000 | % | ISO 527-2/1BA/50 |
| Flexural Modulus (2.00 mm, Compression Molded) | 1550 | MPa | ISO 178 |
| Flexural Stress (2.00 mm, Compression Molded) | 31.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C, Compression Molded | 6.0 | kJ/m² | |
| 23°C, Compression Molded | 10 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 88.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 129 | °C | ISO 306/A |
| Melting Temperature (DSC) | 134 | °C | ISO 11357-3 |
| Enthalpy Change | 223 | J/g | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Blow Molding Barrel Temperature | 175 to 200 | °C | |
| Blow Molding Melt Temperature | 205 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® FM-PF651 | Sumitomo Bakelite Co., Ltd. | Nylon 6 | Sumikon® |
| Lucky Enpla LPB1000D | Lucky Enpla Co LTD | PBT | Lucky Enpla |
| LOXIM 810 02T HB | LOXIM Industries Private Limited | PP, Unspecified | LOXIM |
| LTP ZW-3206 | Chengdu Letian Plastics Co., Ltd | Acetal (POM) Copolymer | LTP |
| Braskem PE SLH0820/30AF | Braskem | LLDPE | Braskem PE |