EPLAMID 66 GFS 30 HS NC
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | EPSAN Plastik SAN. ve TiC. A.S. |
| Trademark: | EPLAMID 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SYxXM4_EPLAMID-66-GFS-30-HS-NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 66, reinforced with 30% of glass fiber, heat stabilized, lubricated, for injection moulding. Eplamid 66 GFS 30 HS is used in all sectors of industry, offering a perfect balance of thermal and mechanical properties. This product is available in natural and in colours on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.35 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 3.00mm | 0.50 | -- | % | ISO 294-4 |
| Flow direction : 3.00mm | 0.30 | -- | % | ISO 294-4 |
| Moisture Content | 0.20 | -- | % | ISO 15512 |
| Ash Content | 30 | -- | % | ISO 3451-4 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 88 | -- | ISO 868 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9100 | 8900 | MPa | ISO 527-2/50 |
| Tensile Stress (Break, 23°C) | 185 | 175 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 2.0 | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 8850 | 8750 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 255 | 235 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | 16 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 14 | 15 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 3 | ||||
| 0.45 MPa, not annealed | 245 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 235 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 240 | -- | °C | ISO 306/B120 |
| Melting Temperature (DSC) | 250 | -- | °C | ISO 3146 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94, IEC 60695-11-10, -20 |
| Additional Information |
|---|
| 干燥 TEST CONDITIONS: Laboratory conditions are 23 ±2°C and 45-55 % RH. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 280 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren F200 (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Sinvicomp SFW6000 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Fiberfil® PP-61/CC/20 | Fiberfil® Engineered Plastics Inc. | PP Copolymer | Fiberfil® |
| Hax™ HFX 509/1 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
| Polifor® 12 CA/40 NATURALE | SO.F.TER. SPA | PP Homopolymer | Polifor® |