OXNILON 66 30CF 15PTFE
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Oxford Polymers |
| Trademark: | OXNILON 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SY2m2A_OXNILON-66-30CF-15PTFE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| OXNILON 66 30CF 15PTFE is a Polyamide 66 (Nylon 66) material filled with 30% carbon fiber and 15% ptfe fiber. It is available in North America for injection molding. Primary attribute of OXNILON 66 30CF 15PTFE: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.15 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 214 | MPa | |
| Break | 214 | MPa | |
| Flexural Modulus | 17200 | MPa | ASTM D790 |
| Flexural Strength | 310 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (4°C) | 85 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 260 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 249 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | HB | ||
| 3.18 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 104 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 271 to 293 | °C | |
| Middle Temperature | 277 to 299 | °C | |
| Front Temperature | 282 to 304 | °C | |
| Processing (Melt) Temp | 282 to 299 | °C | |
| Mold Temperature | 65.6 to 104 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makropol® PC A3 G20 PRTA010 PC315 | Petropol Industry and Trade of Polymers LTDA | PC | Makropol® PC |
| Ranger PBT PBT-403-M-G30 HF | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| SHIN-A SCT-150M70 | SHIN-A T&C | Epoxy | SHIN-A |
| Bayfit® 566 (80 Index, 2.8 pcf) | Covestro - PUR | PUR-Ether/MDI | Bayfit® |
| Braskem PP C7069-100NA | Braskem Europe GmbH | PP Impact Copolymer | Braskem PP |