Generic Phenolic
| Category: | Phenolic , Phenolic |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SXcRB6_Generic-Phenolic.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Phenolic This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.02 - 1.56 | g/cm³ | ASTM D792 |
| 23°C | 1.35 - 1.85 | g/cm³ | ISO 1183 |
| Apparent Density | 0.54 - 1.24 | g/cm³ | ASTM D1895 |
| Bulk Factor | 2.0 - 8.0 | ASTM D1895 | |
| Molding Shrinkage | |||
| Flow : 23°C | 0.28 - 1.2 | % | ASTM D955 |
| 23°C | 0.10 - 9.5 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.020 - 0.54 | % | ASTM D570 |
| 23°C, 24 hr | 0.035 - 0.40 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 42 - 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 6760 - 20200 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield, 23°C | 45.9 - 112 | MPa | ASTM D638 |
| 23°C | 46.9 - 60.2 | MPa | ASTM D638 |
| 23°C | 54.5 - 60.5 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 5730 - 18400 | MPa | ASTM D790 |
| Flexural Strength | |||
| 23°C | 68.9 - 159 | MPa | ASTM D790 |
| 23°C | 77.0 - 176 | MPa | ISO 178 |
| Yield, 23°C | 76.7 - 131 | MPa | ASTM D790 |
| Compressive Strength | |||
| 23°C | 48.3 - 236 | MPa | ASTM D695 |
| 23°C | 190 - 295 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23°C | 33.2 - 83.6 | J/m | ASTM D256 |
| 23°C | 1.6 - 9.8 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 15 - 92 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 159 - 205 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 155 - 300 | °C | ISO 75-2/A |
| Melting Temperature | 65.0 - 75.2 | °C | |
| CLTE - Flow | 1.8E-5 - 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 150 - 160 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | |||
| 23°C | 1.0E+11 - 1.3E+13 | ohms·cm | ASTM D257 |
| 23°C | 8.4E+11 - 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 8.7 - 20 | kV/mm | ASTM D149 |
| 23°C | 9.9 - 15 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 4.44 - 6.60 | ASTM D150 | |
| 23°C | 5.00 - 6.50 | ASTM D2520 | |
| 23°C | 4.83 | IEC 60250 | |
| Dissipation Factor (23°C) | 0.023 - 0.087 | ASTM D150 | |
| Arc Resistance | 0.00 - 192 | sec | ASTM D495 |
| Comparative Tracking Index | 175 - 225 | V | IEC 60112 |
| Insulation Resistance (23°C) | 1.0E+8 - 1.0E+11 | ohms | IEC 60167 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Mix Viscosity | 26.5 - 1370 | cP | ASTM D2393 |
| Post Cure Time | 4.9E-3 - 1.3 | hr |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 67.5 - 75.0 | °C | |
| Front Temperature | 90.0 - 95.0 | °C | |
| Mold Temperature | 173 - 175 | °C | |
| Screw Speed | 50 - 60 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PhenolicThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TYNAB® HM42 | Tyne Plastics LLC. | ABS | TYNAB® |
| Fainplast PVC HGKA 81 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Okirol® E-5 | DIOKI d.d. | PS (EPS) | Okirol® |
| O'Tech OW 822 | O'Tech Corporation | PVC, Unspecified | O'Tech |
| Sylvin 83019-80UV Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |