Aristech ALTAIR PLUS® (0.160 inch)
| Category: | ABS+Acrylic , Acrylonitrile Butadiene Styrene + Acrylic (PMMA) |
| Manufacturer: | Aristech Acrylics LLC |
| Trademark: | Aristech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SXZnGF_Aristech-ALTAIR-PLUS-0-160-inch-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aristech Acrylics LLC Altair Plus® is a composite engineered material which has the exceptional surface properties, weathering characteristics and aesthetics of Aristech Acrylics LLC Opaque Continuous Cast Acrylic and a substrate that imparts outstanding impact resistance and thermoformability. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.09 | g/cm³ | ASTM D792 |
| Water Absorption (Saturation, 4.10 mm) | 0.19 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale, 4.10 mm) | 67 | ASTM D785 | |
| Barcol Hardness (4.10 mm) | 54 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (4.10 mm) | 2550 | MPa | ASTM D638 |
| Tensile Strength (Yield, 4.10 mm) | 45.5 | MPa | ASTM D638 |
| Tensile Elongation (Break, 4.10 mm) | 4.4 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 4.10 mm 2 | 2250 | MPa | |
| 4.10 mm 3 | 2340 | MPa | |
| Flexural Strength | ASTM D790 | ||
| 4.10 mm 4 | 74.5 | MPa | |
| 4.10 mm 5 | 62.7 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (4.10 mm) | 110 | J/m | ASTM D256A |
| Instrumented Dart Impact 6(4.10 mm) | 16.7 | J | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.10 mm) | 85.6 | °C | ASTM D648 |
| CLTE - Flow (4.10 mm) | 8.5E-5 | cm/cm/°C | ASTM D696 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°, 4.10 µm) | 87 | ASTM D523 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Forming Temperature | Internal Method | ||
| ABS Side : 4.10 mm | 149 to 171 | °C | |
| Acrylic Side : 4.10 mm | 177 to 193 | °C | |
| Odor (4.10 mm) | None |
| Note Message | |
|---|---|
| 1 . | .160 inch |
| 2 . | Acrylic in Tension |
| 3 . | Acrylic in Compression |
| 4 . | Acrylic in Tension |
| 5 . | Acrylic in Compression |
| 6 . | FTMS 406-M-1074 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIREX® Compound 3500G30 | Samyang Corporation | PC | TRIREX® Compound |
| WEVO-CHEMIE Polyurethanes PU 403 FL/300 RE | WEVO-CHEMIE GmbH | PUR, Unspecified | WEVO-CHEMIE Polyurethanes |
| CP PRYME® Nylon 6 N120L | Chase Plastics Services Inc. | Nylon 6 | CP PRYME® Nylon 6 |
| HiFill® PBT GF30 | Techmer Engineered Solutions | PBT | HiFill® |
| Monprene® CP-11140 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |