Vyncolit® X6151 Datasheet,Phenolic,Vyncolit N.V.-SHANGHAI SUSHENG

Message
Vyncolit X6151 is a phenolic molding compound with excellent mechanical properties and good flexibility.

General Information
Filler / Reinforcement	Glass \Mineral
Features	Good flexibility
Appearance	Black
Forms	Particle
Processing Method	Resin transfer molding Compression molding Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.55	g/cm³	ISO 1183
Molding Shrinkage - Flow	0.25 - 0.35	%	ISO 294-4
Water Absorption (23°C, 24 hr)	0.15	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (Injection Molded)	12000	MPa	ISO 527-2
Tensile Stress (Break, Injection Molded)	70.0	MPa	ISO 527-2
Tensile Strain (Break, Injection Molded)	0.80	%	ISO 527-2
Flexural Modulus (Injection Molded)	10000	MPa	ISO 178
Flexural Stress (Injection Molded)	170	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (Injection Molded)	4.0	kJ/m²	ISO 179
Charpy Unnotched Impact Strength	13	kJ/m²	ISO 179

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
1.8 MPa, not annealed	190	°C	ISO 75-2/A
8.0 MPa, not annealed	160	°C	ISO 75-2/C
Linear thermal expansion coefficient			ASTM E831
Flow	2.5E-5	cm/cm/°C	ASTM E831
Lateral	4.5E-5	cm/cm/°C	ASTM E831

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength	30	kV/mm	IEC 60243-1
Comparative Tracking Index	175	V	IEC 60112

Flammability	Nominal Value	Test Method
Flame Rating		UL 94
1.60 mm	V-1	UL 94
4.00 mm	V-0	UL 94

Injection	Nominal Value	Unit
Rear Temperature	60.0	°C
Middle Temperature	73.9	°C
Nozzle Temperature	87.8	°C
Processing (Melt) Temp	98.9 - 116	°C
Mold Temperature	166 - 188	°C
Injection Pressure	100 - 248	MPa
Holding Pressure	30.0 - 89.6	MPa
Back Pressure	4.83 - 15.2	MPa

Injection instructions
Plastication: 50rpmInjection Time: 2 to 8 secHold Time: 1 to 5 sec/mmCure Time, 0.125 in: 5 to 12 sec/mmAll ISO properties listed were tested in accordance with ISO 3167The value listed as Molding Shrinkage, ISO 294-4, was tested in accordance with ISO 2577.ISO Type: PF 2 C3Powder Density, ISO 60: 0.6 to 0.75 g/cm³Post Shrinkage, ISO 2577: 0.05 to 0.15%HDT A (1.80 MPa) Unannealed, ISO 75A, Injection Molding: 180 to 200°CHDT A (8.0 MPa) Unannealed, ISO 75A, Injection Molding: 150 to 170°CCLTE, Flow (TMA), ASTM E831, Injection Molding: 20 to 30 cm^-6/cm°CCLTE, Transverse (TMA), ASTM E831, Injection Molding: 40 to 50 cm^-6/cm°CFlexural Strength, ISO 178, Injection Molding: 160 to 180 MPaFlexural Modulus, ISO 178, Injection Molding: 9 to 11 GPaStrain to failure in Flexure, ISO 178, Injection Molding: 1.7 to 1.8%Tensile Stress at Break, ISO 527-1,-2, Injection Molding: 60 to 80 MPaTensile Modulus, ISO 527-1,-2, Injection Molding: 11 to 13 GPaTensile Strain at Break, ISO 527-1,-2, Injection Molding: 0.75 to 0.85%Charpy Notched Impact Strength, ISO 179, Injection Molding: 3 to 5 kJ/m²Charpy Unnotched Impact Strength, ISO 179, Injection Molding: 12 to 14 kJ/m²Compressive Strength, ISO 604: 220 to 250 MPa

Injection instructions

Plastication: 50rpmInjection Time: 2 to 8 secHold Time: 1 to 5 sec/mmCure Time, 0.125 in: 5 to 12 sec/mmAll ISO properties listed were tested in accordance with ISO 3167The value listed as Molding Shrinkage, ISO 294-4, was tested in accordance with ISO 2577.ISO Type: PF 2 C3Powder Density, ISO 60: 0.6 to 0.75 g/cm³Post Shrinkage, ISO 2577: 0.05 to 0.15%HDT A (1.80 MPa) Unannealed, ISO 75A, Injection Molding: 180 to 200°CHDT A (8.0 MPa) Unannealed, ISO 75A, Injection Molding: 150 to 170°CCLTE, Flow (TMA), ASTM E831, Injection Molding: 20 to 30 cm^-6/cm°CCLTE, Transverse (TMA), ASTM E831, Injection Molding: 40 to 50 cm^-6/cm°CFlexural Strength, ISO 178, Injection Molding: 160 to 180 MPaFlexural Modulus, ISO 178, Injection Molding: 9 to 11 GPaStrain to failure in Flexure, ISO 178, Injection Molding: 1.7 to 1.8%Tensile Stress at Break, ISO 527-1,-2, Injection Molding: 60 to 80 MPaTensile Modulus, ISO 527-1,-2, Injection Molding: 11 to 13 GPaTensile Strain at Break, ISO 527-1,-2, Injection Molding: 0.75 to 0.85%Charpy Notched Impact Strength, ISO 179, Injection Molding: 3 to 5 kJ/m²Charpy Unnotched Impact Strength, ISO 179, Injection Molding: 12 to 14 kJ/m²Compressive Strength, ISO 604: 220 to 250 MPa

Category:	Phenolic , Phenolic
Manufacturer:	Vyncolit N.V.
Trademark:	Vyncolit®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	SX9vOb_Vyncolit-X6151.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 304 TFE 10 FR A	RTP Company	PC	RTP
VECTOR® 4186A	Dexco Polymers LP	SI	VECTOR®
Lion Idemitsu Composites PPS C-600SG	Lion Idemitsu Composites Co., Ltd.	PPS	Lion Idemitsu Composites PPS
PETILEN YY F 00556 (HMW)	PETKIM Petrokimya Holding A.S.	HDPE	PETILEN
ALTECH® PA6 A 2030/320.01 GF30 UV	ALBIS PLASTIC GmbH	Nylon 6	ALTECH® PA6