POLYblend PC/ABS 65H
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYblend |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SUycBU_POLYblend-PC-ABS-65H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/ABS-blend |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 23 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.50 to 0.70 | % | |
| Flow | 0.50 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 61.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 8.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2500 | MPa | ISO 178 |
| Flexural Stress | 96.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 17 | kJ/m² | |
| 23°C | 48 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 121 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 123 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 102 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 107 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 134 | °C | ISO 306/A50 |
| -- | 120 | °C | ISO 306/B50 |
| Ball Pressure Test (110°C) | Pass | IEC 60695-10-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 650 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Chansieh Phenolic P-110 | Chansieh Enterprises Co., LTD. | Phenolic | Chansieh Phenolic |
| Keltan® 6160D | LANXESS Buna GmbH | EPDM | Keltan® |
| Hylex® P1310G7FRMA | Ravago Manufacturing Americas, LLC | PC | Hylex® |
| Karina BLACK PVC COMPOUND 956-48/1-C-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plexiglas® V045 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |