OREVAC® 18341 is a maleic anhydride modified linear low-density polyethylene. It is available in pellet form for use in conventional extrusion equipment designed to process polyolefin. Applications OREVAC® 18341 has been designed to develop a reliable bonding strength between polyethylene or ethylene copolymers and mineral fillers such as aluminum trihydrate (ATH) or magnesium hydroxide (MDH). It is an effective coupling agent for halogen-free flame retardant compounds using high loadings of mineral fillers, such as compounds for insulation and sheathing of wires and cables. OREVAC® 18341 can also be used as a tie layer in pipe-coating technology for multi-layer structures. It has been designed to develop a reliable bonding strength onto FBE (Fusion Bonded Epoxy) steel pipe protective layer. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.3 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shore D, 1 sec, Compression Molded | 55 | ||
| Shore D, 15 sec, Compression Molded | 45 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 250 | MPa | ASTM D638, ISO 527-2/1A |
| Tensile Strength (Break, Compression Molded) | > 20.0 | MPa | ASTM D638, ISO 527-2/1A |
| Tensile Elongation (Break, Compression Molded) | > 600 | % | ASTM D638, ISO 527-2/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature 1 | 95.0 | °C | ISO 306/A, ASTM D1525 2 |
| Melting Temperature | 121 | °C | ISO 11357-3 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 180 to 190 | °C | |
| Cylinder Zone 2 Temp. | 190 to 200 | °C | |
| Cylinder Zone 3 Temp. | 200 to 210 | °C | |
| Cylinder Zone 4 Temp. | 210 to 220 | °C | |
| Cylinder Zone 5 Temp. | 220 to 230 | °C | |
| Die Temperature | 220 to 240 | °C |
| Note Message | |
|---|---|
| 1 . | On compression molded samples |
| 2 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Niblan V100 AE V0/M | Soredi S.p.a. | PBT | Niblan |
| Nylene® CX3395 | Custom Resins Group | Nylon 6 | Nylene® |
| Boda BDPL-H4701 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Epolene® C-16 | Westlake Chemical Corporation | LDPE | Epolene® |
| Lupox® GP2100 | LG Chem Ltd. | PBT | Lupox® |