LNP™ LUBRILOY™ Z2000 compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRILOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SSiHGb_LNPLUBRILOYZ2000compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRILOY Z2000 is a compound based on PPE+PS Blend resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRILOY* Compound Z Product reorder name: Z2000 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.89 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.2 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.2 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.89 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.064 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.072 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1820 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 47.0 | MPa | ASTM D638 |
| Yield | 38.0 | MPa | ISO 527-2 |
| Fracture | 42.4 | MPa | ASTM D638 |
| Fracture | 41.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 4.2 | % | ASTM D638 |
| Yield | 3.2 | % | ISO 527-2 |
| Fracture | 52 | % | ASTM D638 |
| Fracture | 37 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2090 | MPa | ASTM D790 |
| -- | 1860 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 74.3 | MPa | ASTM D790 |
| -- | 58.8 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.19 | ASTM D3702 Modified | |
| With Self-Static | 0.24 | ASTM D3702 Modified | |
| Wear Factor - Washer | 121 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 110 | J/m | ASTM D256 |
| 23°C 1 | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 2000 | J/m | ASTM D4812 |
| 23°C 2 | 170 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 141 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 3 | 138 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 122 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 120 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 8.2E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 8.9E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 254 - 266 | °C | |
| Middle Temperature | 260 - 271 | °C | |
| Front Temperature | 266 - 277 | °C | |
| Processing (Melt) Temp | 277 - 293 | °C | |
| Mold Temperature | 60.0 - 93.3 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Axiall PVC 15644 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Plaskon CMU-870-2C | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |
| Sylvin 8362-75 Brown 7437 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Dow Corning® MG-2402 | Dow Corning Corporation | Silicone | Dow Corning® |
| SCHULABLEND® (ABS/PA) M/MK 6101 GF8 U | A. Schulman Europe | ABS+Nylon | SCHULABLEND® |