Sumikon® FM-MK104

Category: PPS , Polyphenylene Sulfide
Manufacturer: Sumitomo Bakelite Co., Ltd.
Trademark: Sumikon®
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: SSMnc6_Sumikon-FM-MK104.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
PPS molding compounds developed for the purpose of metal substituion. They currently are extensively used in precision molded parts such as optical parts.
General Information
Filler / Reinforcement
  • Glass fiber reinforced material
Features
  • General
Uses
  • Metal substitution
  • Printing machine parts
Forms
  • Particle
PhysicalNominal ValueUnitTest Method
Specific Gravity 1.64g/cm³ASTM D792
Molding Shrinkage ASTM D955
    Flow 0.20%ASTM D955
    Transverse flow 0.60%ASTM D955
Water Absorption (23°C, 24 hr)0.20%ASTM D570
HardnessNominal ValueUnitTest Method
Rockwell Hardness (R-Scale)120ASTM D785
MechanicalNominal ValueUnitTest Method
Tensile Strength (Yield)129MPaASTM D638
Tensile Elongation (Yield)1.2%ASTM D638
Flexural Modulus 12000MPaASTM D790
Flexural Strength (Yield)178MPaASTM D790
ImpactNominal ValueUnitTest Method
Notched Izod Impact 92J/mASTM D256
ThermalNominal ValueUnitTest Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)260°CASTM D648
Thermal Conductivity 0.70W/m/KASTM C177
ElectricalNominal ValueUnitTest Method
Volume Resistivity 1.0E+16ohms·cmASTM D257
Dielectric Strength 17kV/mmASTM D149
Dielectric Constant (1 MHz)4.00ASTM D150
Dissipation Factor (1 MHz)1.4E-3ASTM D150
Arc Resistance 125secASTM D495
FlammabilityNominal ValueUnitTest Method
Flame Rating V-0UL 94
InjectionNominal ValueUnit
Drying Temperature 120°C
Drying Time 3.0hr
Mold Temperature 120 - 150°C
Injection instructions
Cylinder temperature: 290 to 340°C
Resin Grade Manufacturer Category Trademark
TUFNYL® SGF 15 GA BLACK SRF Ltd. Nylon 6 TUFNYL®
Flontech® FLON-5117-1 Guarniflon S.p.A. - Flontech Division PTFE Flontech®
Elastron® D D100.A30.B Elastron USA, Inc. SBS Elastron® D
Kingfa MAC-601 UV Kingfa PC+ABS Kingfa
Lutene® H BE0400 LG Chem Ltd. HDPE Lutene® H