DINALEN® 30
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | DIOKI d.d. |
| Trademark: | DINALEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SSKglf_DINALEN-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DINALEN® 30 is low density polyethylene containing no additives. It is primarily intended for blow film extrusion while other processing techniques can be used to a lesser extent. DINALEN® 30 exhibits very good draw-down with good balance of stiffness, mechanical and optical properties of extruded film. DINALEN® 30 is extruded at recommended melt temperature range between 165°C and 185°C. Recommended film thickness: 0.030 mm to 0.100 mm. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 45 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 200 | MPa | ISO 527-2/200 |
| Tensile Stress | ISO 527-2/200 | ||
| Yield, Compression Molded | 11.0 | MPa | |
| Break, Compression Molded | 16.0 | MPa | |
| Tensile Strain (Break, Compression Molded) | 650 | % | ISO 527-2/200 |
| Coefficient of Friction | ISO 8295 | ||
| vs. Itself - Dynamic | > 0.40 | ||
| vs. Itself - Static | > 0.40 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Film Thickness - Recommended / Available | 0.030 mm to 0.100 mm | ||
| Tensile Strength | ISO 527-3/500 | ||
| TD : Blown Film | 18.0 | MPa | |
| MD : 50 µm, Blown Film | 23.0 | MPa | |
| Tensile Elongation | ISO 527-3/500 | ||
| MD : Break, 50 µm, Blown Film | 220 | % | |
| TD : Break, 50 µm, Blown Film | 320 | % | |
| Dart Drop Impact (50 µm, Blown Film) | 250 | g | ISO 7765-1 |
| Trouser Tear Resistance 1 | ISO 6383-1 | ||
| MD : 50 µm, Blown Film | 93.0 | N/mm | |
| TD : 50 µm, Blown Film | 58.0 | N/mm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 94.0 | °C | ISO 306/A50 |
| Melting Temperature | 114 | °C | ISO 11357-3 |
| Optical | Nominal Value | ||
|---|---|---|---|
| Gloss | |||
| 20°, 50.0 µm, Blown Film | > 50 | ||
| 60°, 50.0 µm, Blown Film | > 100 |
| Note Message | |
|---|---|
| 1 . | 250 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2700 S-60A | RTP Company | SEBS | RTP |
| Rotec® ABS 1001 TR-AC F | ROMIRA GmbH | ABS | Rotec® ABS |
| Star L PA6 D36 | Eurostar Engineering Plastics | Nylon 6 | Star L |
| Thermoset Plastics 261 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| Sylvin 9067A-90 Grey 9166 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |