| Polyamide 6 black with 20% glass fibre reinforcement and protected against ultra violet rays (UV). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.40 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 1.1 | % | ISO 62 |
| Ash Content | 20 | % | Internal Method |
| Humidity - Pellets | 0.20 | % | ISO 1110 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 78 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6900 | MPa | ISO 527-2 |
| Tensile Stress | 120 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 210 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 180 | °C | ISO 75-2/A |
| Vicat Softening Temperature | > 210 | °C | ISO 306 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Electric Strength | 22 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 230 to 240 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA III PPJ500 | ROMPETROL PETROCHEMICALS S.R.L. | PP Homopolymer | MIDILENA III |
| Shin-Etsu Elastomer KE-2095-50A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Nypol® PA B3 HL AZL0309 NT360 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| LONGLITE® PMC T 385 J70 | CCP Group | Phenolic | LONGLITE® PMC |
| Sylvin 8600-64D Grey 9456 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |