Lupoy® SG5009F
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SRXTMr_Lupoy-SG5009F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description High Gloss, Scratch Resistance, Halogen Free Flame Retardent Application IT/OA(Notebook PC & Monitor housing) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 58.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | > 100 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2670 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 98.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm) | 90.0 | °C | ASTM D648 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 230 to 270 | °C | |
| Middle Temperature | 235 to 275 | °C | |
| Front Temperature | 235 to 275 | °C | |
| Nozzle Temperature | 235 to 272 | °C | |
| Processing (Melt) Temp | 245 to 275 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Back Pressure | 0.981 to 1.96 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NaturePlast NP EL 007 | NaturePlast | TPE | NaturePlast |
| CP PRYME® Nylon 66 NN333HSL BK-P | Chase Plastics Services Inc. | Nylon 66 | CP PRYME® Nylon 66 |
| Okirol® E-6 | DIOKI d.d. | PS (EPS) | Okirol® |
| POLYCASA® XT Soft Tone | Polycasa | Acrylic (PMMA) | POLYCASA® |
| CarbonResin PR 25 | Carbon3D, Inc. | Unspecified | CarbonResin |