Geon™ HTX LA550
| Category: | PVC Alloy , Polyvinyl Chloride Alloy |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ HTX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SR3sbs_Geon-HTX-LA550.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Geon HTX LA550 is a PVC Alloy suitable for darker colors and horizontal applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 81 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2240 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 46.2 | MPa | ASTM D638 |
| Flexural Modulus | 2280 | MPa | ASTM D790 |
| Flexural Strength | 68.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Compression Molded) | 120 | J/m | ASTM D256A |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C 3 | 49.4 | J/cm | ASTM D4226 |
| 23°C 4 | > 178 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, annealed, 3.18mm 5 | 84.4 | °C | ASTM D648 |
| 0.45 MPa, annealed, 3.18mm 6 | 83.9 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm 7 | 75.6 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm 8 | 77.2 | °C | ASTM D648 |
| CLTE - Flow | 8.5E-5 | cm/cm/°C | ASTM D696 |
| Additional Information |
|---|
| Physical properties based on Geon HTX LA550 Brown 3566. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 193 - 204 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | Procedure A, C.125 Throwing |
| 4 . | Procedure B, C.125 Throwing |
| 5 . | Annealed at 50 deg.C |
| 6 . | Annealed at 60 deg.C |
| 7 . | Annealed at 50 deg.C |
| 8 . | Annealed at 60 deg.C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TABOREN PH 72 T 40 | SILON s.ro | PP Homopolymer | TABOREN |
| NOVA PC HM2045 | NOVA Polymers, Inc. | PC | NOVA PC |
| CGPC PVC R-11X HI Extrusion | China General Plastics Corporation | PVC, Flexible | CGPC PVC |
| EXCELLEN® GMH CB1001 | Sumitomo Chemical Asia | PE, Unspecified | EXCELLEN® GMH |
| LubriOne™ NN-10GF/10T BLACK | PolyOne Corporation | Nylon 66 | LubriOne™ |