GLS ABS SN08
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | GLS Polymers Pvt. Ltd. |
| Trademark: | GLS ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SQyhaK_GLS-ABS-SN08.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABS FR V2 |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 to 1.12 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | > 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | > 48.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | > 1900 | MPa | ASTM D790 |
| Flexural Strength 3 | > 60.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | > 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 86.0 | °C | ASTM D648 |
| Vicat Softening Temperature | > 96.0 | °C | ASTM D1525 4 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 206 to 236 | °C | |
| Mold Temperature | 65.0 to 86.0 | °C | |
| Injection Pressure | 70.0 to 101 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | Rate B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sofprene T® 540200A50 | SO.F.TER. SPA | SBS | Sofprene T® |
| APEX® 1850 | Teknor Apex Company | PVC, Flexible | APEX® |
| Gallonprene® GP200-8 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Hostaform® C 27021 AS | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Jackdaw PLA HT16WT6652 | Jackdaw Polymers | PLA | Jackdaw PLA |