SABIC® PP 670Kh
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SQwOck_SABIC-PP-670Kh.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PP 670Kh is a polypropylene random copolymer grade with medium melt flow intended for producing injection-moulded articles of high clarity. This product is formulated with an additive package, which enables a reduced cooling time in combination with high demoulding temperature. Products from SABIC® PP 670Kh have a very high clarity, a good impact strength-stiffness balance and good organoleptic properties. Closures from SABIC® PP 670Kh have excellent hinge strength. SABIC® PP 670Kh typically is used in caps & closures, lids, housewares, and appliances. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 11 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 94 | ASTM D785 | |
| Shore Hardness (Shore D) | 64 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant 1 | 1150 | MPa | ASTM D638 |
| -- | 1050 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 2 | 28.0 | MPa | ASTM D638 |
| Yield | 27.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 3 | 14 | % | ASTM D638 |
| Yield | 14 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0°C | 2.0 | kJ/m² | |
| 23°C | 6.5 | kJ/m² | |
| Notched Izod Impact | |||
| 0°C | 30 | J/m | ASTM D256A |
| 23°C | 60 | J/m | ASTM D256A |
| 0°C | 2.5 | kJ/m² | ISO 180/1A |
| 23°C | 6.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 80.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 75.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 55.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 50.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 126 | °C | ASTM D1525, ISO 306/A120 6 6 |
| -- | 69.0 | °C | ASTM D1525, ISO 306/B120 7 7 |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Retpol® 7573 UVH | PolyPacific Pty. Ltd. | PP, Unspecified | Retpol® |
| Axpoly® PP19 1033 | Axion Polymers | PP Homopolymer | Axpoly® |
| Karina IVORY PVC COMPOUND 939-35/ 1-CY-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina MBPEBD BLACK -E 4800/ 3-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 83015-80FUV Brown 7463 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |