AXELERON™ CX K-0012 NT

Category:	LDPE , Nucleating Agent Masterbatch
Manufacturer:	The Dow Chemical Company
Trademark:	AXELERON™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	SQvTYK_AXELERON-CX-K-0012-NT.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
DOW™AXELERON™CX K-0012 NT is a masterbatch, which is used as a nucleating agent in gas injection processing. It is specially developed for easy mixing with HDPE and LDPE. When used, a small, evenly distributed cell structure can be made. The masterbatch is based on high-pressure LDPE resin, and 2% of a heating chemical foaming agent is added. The usage of this product should be 0.5-3% masterbatch content. DOW™AXELERON™CX K-0012 NT contains a stabilizer to prevent thermal oxidation and copper-induced catalyst degradation. Application areas: Typical application areas include RF cables and CATV lead-in cables, with a foaming rate of up to 80%.

General Information
Uses	Coaxial Cable Insulation Wire and cable applications Insulating material Masterbatch Foam Communication Equipment
Forms	Particle
Processing Method	Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.928	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) ¹(140°C/2.16 kg)	1.7	g/10 min	ISO 1133

Extrusion	Nominal Value	Unit
Melt Temperature	170 - 190	°C

Extrusion instructions
Dow AXELERON™ CX K-0012 NT Polyethylene Masterbatch is designed to be extruded with HDPE DGDA-6944 NT and LDPE DFDK-1253 NT from Dow. It is normally added at 0.5 - 3 % masterbatch concentration into a blend of 60 - 80 % DGDA-6944 NT and 20 - 40 % DFDK-1253 NT. It is normally extruded with a target melt temperature of 170 - 190 °C. Typical extruder barrel temperatures required depend on the extruder size and construction being made but a good starting point is: Feed zone: 140 -150 °C Transition zone: 160 -170 °C Injection point: 180 -190 °C Metering zone: 180 -190 °C Crosshead and Die: 180 -190 °C

Extrusion instructions

Dow AXELERON™ CX K-0012 NT Polyethylene Masterbatch is designed to be extruded with HDPE DGDA-6944 NT and LDPE DFDK-1253 NT from Dow. It is normally added at 0.5 - 3 % masterbatch concentration into a blend of 60 - 80 % DGDA-6944 NT and 20 - 40 % DFDK-1253 NT. It is normally extruded with a target melt temperature of 170 - 190 °C. Typical extruder barrel temperatures required depend on the extruder size and construction being made but a good starting point is: Feed zone: 140 -150 °C Transition zone: 160 -170 °C Injection point: 180 -190 °C Metering zone: 180 -190 °C Crosshead and Die: 180 -190 °C

Note Message
1 .	Measured on MFR cut-off without annealing.

Resin Grade	Manufacturer	Category	Trademark
Spartech Polycom Free Flow	Spartech Polycom	PVC Alloy	Spartech
DIOSHY® TPEE E963D-HD	DIOSHY Co.,Ltd.	TPEE	DIOSHY®
Indothene LL 20FA020	Reliance Industries Limited	LLDPE	Indothene LL
PERLER® O07H1500B11	A.D. Compound S.p.A.	PP Copolymer	PERLER®
Sylvin 4200-88 Red 6287	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin