VYPET VNT 615 FR
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Lavergne Group |
| Trademark: | VYPET |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SOHlib_VYPET-VNT-615-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vypet VNT 615 FR is a 15% fiberglass reinforced flame retardant PET injection molding compound designed for electrical and structural applications Features
Typical Applications
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.90 | % | |
| Flow : 2.00 mm | 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 105 | MPa | ISO 527-2/5 |
| Flexural Modulus 1 | 5900 | MPa | ISO 178 |
| Flexural Stress 2 | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 6.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 200 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+18 | ohms·cm | ASTM D257 |
| Dielectric Strength | 37 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 3.30 | ASTM D150 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.850 mm | V-0 | ||
| 1.50 mm | V-0 5VA | ||
| 3.00 mm | V-0 5VA | ||
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 900 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 265 to 275 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Nozzle Temperature | 275 to 295 | °C | |
| Processing (Melt) Temp | 275 to 295 | °C | |
| Mold Temperature | 95.0 to 120 | °C | |
| Injection Pressure | 55.0 to 85.0 | MPa | |
| Injection Rate | Fast | ||
| Screw Speed | 50 to 75 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ PA6G13-BK10 | Pier One Polymers, Inc. | Nylon 6 | MAXAMID™ |
| Vydyne® 41H BK03 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| AKROMID® B3 3 S3 10 natural (1808) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Capran Medallion庐 MT-2500 | Honeywell | Nylon 6 | Capran Medallion® |
| HiFill FR® PA6/6 GF25 FR BK | Techmer Engineered Solutions | Nylon 66 | HiFill FR® |